Inkampani yethu yamkela inkqubo ye-atomization yegesi ukuvelisa iintlobo ezahlukeneyo ze-Stellite alloy welding powder. I-powder ye-welding ifakwe kumphezulu wamacandelo angaguqukiyo afana nobushushu obuphezulu kunye ne-high-pressure valves, iivalve ze-injini, kunye ne-injini yokutshisa yangaphakathi kunye ne-valve yokukhupha ngokutshiza i-plasma, ukutshiza nge-laser kunye ne-high-velocity oxy-fuel process, ukwenzela ukunyusa ukunyanzeliswa kwezixhobo.
Iinkcukacha zeMveliso
Inkampani yethu yamkela inkqubo ye-atomization yegesi ukuvelisa iintlobo ezahlukeneyo ze-Stellite alloy welding powder. I-powder ye-welding ifakwe kumphezulu wamacandelo angaguqukiyo afana nobushushu obuphezulu kunye ne-high-pressure valves, iivalve ze-injini, kunye ne-injini yokutshisa yangaphakathi kunye ne-valve yokukhupha ngokutshiza i-plasma, ukutshiza nge-laser kunye ne-high-velocity oxy-fuel process, ukwenzela ukunyusa ukunyanzeliswa kwezixhobo.
Ukubunjwa kwemichiza kunye neempawu eziqhelekileyo
Iinkalo zeSicelo
I-Stellite alloy welding powder igqunywa kakhulu kubushushu obuphezulu kunye ne-high-pressure valves, amakhonkco esihlalo sevalve, iivalvu ze-injini, i-injini yokutshisa yangaphakathi kunye ne-valve yokukhupha, ii-injini ze-injini, iibheringi kunye namanye amacandelo ngokutshiza nge-thermal, ukufakwa kwe-laser kunye nezinye iindlela zokuphucula ukuxhathisa ukunxiba kwezi ndawo.
Izinto eziluncedo kunye neeNkonzo
I-Stellite alloy powder eveliswe yinkampani yethu ibonakalisa ukuhanjiswa kobungakanani bamasuntswana afanayo, umxholo ophantsi we-oksijini kunye ne-powder sphericity ephezulu.
| IBanga | C | Si | Mnu | Cr | Ni | Mo | W | Fe | Co | Ubuninzi/g/cm3 | Ukuqina/HRC |
| I-Stellite 1 | 2.0-2.8 | 2.0 | 1.0 | 29-33 | 3.0 | 1.0 | 11.0-14.0 | 3.0 | UBhal. | 8.55 | 51 ~ 55 |
| I-Stellite 3 | 2.0-2.7 | 1.0 | 1.0 | 29-33 | 3.0 | 1.0 | 11.0-14.0 | 3.0 | UBhal. | 8.55 | 51 ~ 55 |
| I-Stellite 6 | 0.9-1.4 | 1.5 | 1.0 | 27-31 | 3.0 | 1.5 | 3.5 ~ 5.5 | 3.0 | UBhal. | 8.30 | 38-44 |
| I-Stellite 20 | 2.2–3.0 | 2.0 | – | 30-34 | 3.0 | 1.0 | 14 ~ 19 | 3.0 | UBhal. | 8.70 | 56-60 |